Anticrater agent for electrocoat composition

ABSTRACT

The present disclosure relates to an improved electrocoating coating composition wherein the improvement is the addition of a non-water reducible anticrater agent. The non-water reducible anticrater agent is a polyester that is the reaction product of an aliphatic carboxylic acid anhydride, a monofunctional epoxy compound, a monofunctional alcohol and a polyepoxide. The improved electrocoating composition provides cured coatings that have fewer craters and have a smooth surface when compared to coatings utilizing other anticrater additives.

CROSS-REFERENCE TO RELATED APPLICATION

This application claims priority under 35 U.S.C. §119 from U.S.Provisional Application Ser. No. 61/431,569, filed Jan. 11, 2011 whichis hereby incorporated by reference in its entirety.

FIELD OF THE DISCLOSURE

The present disclosure is directed to an improved cathodicelectrocoating composition and in particular to an improved cathodicelectrocoating composition wherein the improvement is the incorporationof a non-water reducible anticrater agent, which significantly reducescraters and improves the smoothness of an electrocoated film of thecomposition.

BACKGROUND OF DISCLOSURE

The coating of electrically conductive substrates by an electrocoatingprocess is a well-known and important industrial process. Theelectrocoating of primers to substrates is widely used in the automotiveindustry. In this process, a conductive article, such as an automobilebody or an automobile part, is immersed in a bath comprising an aqueousemulsion of film forming polymer and acts as an electrode in theelectrocoating process. An electric current is passed between thearticle and a counter-electrode in electrical contact with the aqueousemulsion, until a desired coating is deposited on the article. In acathodic electrocoating process, the article to be coated is the cathodeand the counter-electrode is the anode.

Film forming polymer compositions used in the bath of a typical cathodicelectrocoating process are well known in the art. These polymers aretypically made from polyepoxides which have been chain extended usingbisphenol compounds. The chain extended polyepoxides can then be reactedwith amines to form an epoxy amine adduct. These polymers are blendedwith a crosslinking agent and then neutralized with an acid to form awater emulsion, which is usually referred to as a principal emulsion.

The principal emulsion can be combined with a pigment paste, coalescentsolvents, water, and other additives to form the electrocoatingcomposition. The composition is placed in an insulated tank containingthe anode. The article to be coated is the cathode and is placed in atank containing the electrocoating composition. An electrical current isapplied to the system and a layer of the electrocoating composition isdeposited onto the article. The thickness of the applied layer ofelectrocoating composition that is deposited on the article is afunction of, for example, the bath characteristics, the electricaloperating characteristics and the immersion time.

The resulting coated article is removed from the bath after a period oftime and is rinsed with deionized water. The coating on the article canthen be cured, typically in an oven, at sufficient temperature toproduce a crosslinked finish on the article.

Cathodic electrocoating compositions, resin compositions, coating bathsand cathodic processes are disclosed in Jarabek et al U.S. Pat. No.3,922,253 issued Nov. 25, 1975; Wismer et al U.S. Pat. No. 4,419,467issued Dec. 6, 1983; Belanger U.S. Pat. No. 4,137,140 issued Jan. 30,1979 and Wismer et al U.S. Pat. No. 4,468,307 issued Aug. 25, 1984.

A continuing problem with cathodic electrocoating compositions has beenthe presence of craters in the cured finish. A number of anticrateragents have been used in the past to eliminate craters. However, thepresence of conventional anticrater agents in electrocoatingcompositions has had a negative impact on the adhesion of subsequentcoating layers applied thereto, such as automotive PVC sealers used forsealing joints and primer surfacers, particularly where theelectrocoating film has been cured in an oven without the presenceNO_(x) (nitrogen oxides), such as in an indirect gas or electric oven.There is a continuing need for electrocoating compositions that canproduce crater-free, smooth and even finishes that do not adverselyaffecting the adhesion of coatings that are subsequently applied to theelectrocoated substrate.

STATEMENT OF THE DISCLOSURE

The present disclosure is directed to an improved cathodicelectrocoating composition, comprising an aqueous emulsion havingdispersed therein a crosslinkable component and a crosslinking agent;wherein the improvement is the incorporation of a non-water reducibleanticrater agent comprising a polyester which is the reaction product ofa monomer mixture consisting essentially of:

-   -   (a) a cyclic aliphatic carboxylic acid anhydride;    -   (b) a monofunctional epoxy compound;    -   (c) a monofunctional alcohol; and    -   (d) a polyepoxy compound;        wherein the cyclic aliphatic carboxylic acid anhydride contains        one or more side chains selected from the group consisting of an        alkyl side chain having in the range of from 6 to 20 carbon        atoms, an alkenyl side chain having in the range of from 6 to 20        carbon atoms and a combination thereof.

DETAILED DESCRIPTION

The features and advantages of the present disclosure will be morereadily understood, by those of ordinary skill in the art, from readingthe following detailed description. It is to be appreciated that certainfeatures of the disclosure, which are, for clarity, described above andbelow in the context of separate embodiments, may also be provided incombination in a single embodiment. Conversely, various features of thedisclosure that are, for brevity, described in the context of a singleembodiment, may also be provided separately or in any sub-combination.In addition, references in the singular may also include the plural (forexample, “a” and “an” may refer to one, or one or more) unless thecontext specifically states otherwise.

The use of numerical values in the various ranges specified in thisapplication, unless expressly indicated otherwise, are stated asapproximations as though the minimum and maximum values within thestated ranges were both proceeded by the word “about”. In this manner,slight variations above and below the stated ranges can be used toachieve substantially the same results as values within the ranges.Also, the disclosure of these ranges is intended as a continuous rangeincluding every value between the minimum and maximum values.

As used herein:

The phrase “non-water reducible anticrater agent” means that theanticrater agent is free from ionic bonds that result from theneutralization of carboxylic acid groups using an amine or other base.In some embodiments, the non-water reducible anticrater agent has asolubility in water of less than 0.5 grams/liter. In furtherembodiments, the non-water reducible anticrater agent has a solubilityin water of less than 0.1 grams/liter.

It has been found that the addition of the disclosed non-water reducibleanticrater agent can improve the smoothness and reduce the amount ofcraters of a cured layer of electrocoat composition when compared to thesame amount of a water reducible anticrater agents typically used inelectrocoat compositions. In some embodiments, the non-water reducibleanticrater agent is a polyester which is the reaction product of amonomer mixture consisting of or consisting essentially of:

-   -   (a) an aliphatic carboxylic acid anhydride;    -   (b) a monofunctional epoxy compound;    -   (c) a monofunctional alcohol; and    -   (d) a polyepoxy compound.

In some embodiments, the anticrater agent can be formed by 1) contactingan aliphatic carboxylic acid anhydride, a monofunctional epoxy and amonofunctional alcohol at a temperature in the range of from 50° C. to250° C. to form an intermediate polyester followed by the formation ofthe polyester by 2) contacting the intermediate polyester with apolyepoxy compound at a temperature in the range of from 0° C. to 150°C.

An aliphatic carboxylic acid anhydride can be used to form theanticrater agent. In some embodiments, the aliphatic carboxylic acidanhydride can be a cyclic aliphatic carboxylic acid anhydride that issubstituted by one or more alkyl side chains having in the range of from6 to 20 carbon atoms, by one or more alkenyl side chains having in therange of from 6 to 20 carbon atoms, or by a combination thereof, whereinthe side chain can be linear, branched, cyclic or a combination thereof.In some embodiments, the aliphatic carboxylic acid anhydride contains atleast one of the alkyl side chains having in the range of from 8 to 18carbon atoms. In some embodiments, the side chain can also comprise atleast one carbon-carbon double bond. In other embodiments, the aliphaticcarboxylic acid anhydride can include compounds such as those having astructure according to (I);

wherein each R is independently selected from the group consisting of alinear alkyl or alkenyl group having in the range of from 6 to 20 carbonatoms or a branched alkyl or alkenyl group having in the range of from 6to 20 carbon atoms; each R¹ is independently selected from the groupconsisting of hydrogen, a linear alkyl or alkenyl group having in therange of from 6 to 20 carbon atoms, or a branched alkyl or alkenyl grouphaving in the range of from 6 to 20 carbon atoms; or wherein R and R¹may be taken together to form a ring having in the range of from 5 to 6carbon atoms wherein the ring may optionally be substituted with alinear or branched alkyl group having in the range of from 1 to 18carbon atoms or a linear or branched alkenyl group having in the rangeof from 2 to 18 carbon atoms; n is in the range of from 1 to 2; and q isin the range of from 1 to 2. Combinations of any of the aliphaticcarboxylic acid anhydrides can also be used. Suitable aliphaticcarboxylic acid anhydrides can include, for example,methylhexahydrophthalic anhydride, dodecylsuccinic anhydride,octylsuccinic anhydride, hexadecenylsuccinic anhydride, octenylsuccinicanhydride, octadecenylsuccinic anhydride, tetradecenylsuccinicanhydride, dodecenylsuccinic anhydride or a combination thereof. Inother embodiments, the aliphatic carboxylic acid anhydrides include forexample, dodecenylsuccinic anhydride, octadecenylsuccinic anhydride or acombination thereof.

The anticrater agent can be formed from a monomer mixture that includesa monofunctional epoxy compound. In some embodiments, the monofunctionalepoxy can be a monofunctional epoxy ester, for example, the glycidylester of a carboxylic acid or an epoxy ether. In still furtherembodiments, the monofunctional epoxy ester can be the glycidyl ester ofa carboxylic acid wherein the carboxylic acid has a structure accordingto (II);

wherein each R³, R⁴ and R⁵ is independently selected from the groupconsisting of a linear alkyl groups having in the range of from 1 to 12carbon atoms, a branched alkyl group having in the range of from 3 to 12carbon atoms, a cycloaliphatic alkyl group having in the range of from 5to 8 carbon atoms or a combination thereof. In some embodiments, thetotal number of carbon atoms in the combination of R³, R⁴ and R⁵ can bein the range of from 4 to 20. In other embodiments, the total number ofcarbon atoms in the combination of R³, R⁴ and R⁵ can be in the range offrom 7 to 12. Suitable examples of the monofunctional epoxy ester caninclude, for example, the glycidyl esters of pivalic acid, 2,2-dimethylbutyric acid, neodecanoic acid, VERSATIC® acid or a combination thereof.

Other monofunctional epoxy compounds which can be used include, forexample, glycidyl ethers of monohydric alcohols wherein the alcoholscontain in the range of from 4 to 20 carbon atoms or glycidyl ethers ofaromatic monohydric alcohols. Representative examples of glycidyl etherscan include, for example, o-cresyl glycidyl ether, phenyl glycidylether, butyl glycidyl ether, octyl glycidyl ether, dodecyl glycidylether, glycidoxypropyltrimethoxysilane, glycidoxypropyltriethoxysilane,2-ethylhexyl glycidyl ether or a combination thereof.

The anticrater agent can be formed from a monomer mixture that includesa monofunctional alcohol. In some embodiments, the monofunctionalalcohols can include alcohols containing linear, branched,cycloaliphatic alkyl groups or a combination thereof. In furtherembodiments, the monofunctional alcohols can contain in the range offrom 4 to 12 carbon atoms and can be a linear, branched orcycloaliphatic alcohol. In still further embodiments, the monofunctionalalcohols can include, for example, hexanol, 2-methyl butanol,2-ethylhexanol, cyclohexyl methanol, methyl cyclohexanol, cyclohexanol,octanol or a combination thereof.

In some embodiments, the anticrater agent can be produced by firstforming an intermediate polyester. The intermediate polyester can beproduced by contacting a monomer mixture consisting of an aliphatic acidanhydride, a monofunctional epoxy compound, a monofunctional alcohol andoptionally, a catalyst at a temperature in the range of from 50° C. to250° C. for a time period ranging from 10 minutes to 24 hours. A solventcan be used or the formation of the intermediate polyester can beperformed without the use of a solvent. In some embodiments, the ratioof monomers in the monomer mixture can be chosen so that theintermediate polyester contains carboxylic acid groups. In someembodiments, the acid number of the intermediate polyester can be in therange of from 10 mg KOH/g to 300 mg KOH/g. In other embodiments, theacid number of the intermediate polyester can be in the range of from 35mg KOH/g to 275 mg KOH/g, and in still further embodiments, the acidnumber of the intermediate polyester can be in the range of from 50 mgKOH/g to 250 mg KOH/g. In some embodiments, the monomer mixture can beheated until the weight per epoxy group of the intermediate polyester isas high as possible, for example greater than 15,000 Daltons. In otherembodiments, the monomer mixture is heated until the weight per epoxygroup of the intermediate polyester is greater than 17,000 Daltons, andin still further embodiments, until the weight per epoxy group of theintermediate polyester is greater than 18,000 Daltons. The optionalcatalyst can include, for example, triarylphosphines,triphenylphosphine, alkyltriarylphosphonium halides,ethyltriphenylphosphonium halide, alkyltriarylphosphonium esters,ethyltriphenylphosphonium acetate, ethyltriphenylphosphonium diacetate,tetraalkylphosphonium halide or a combination thereof.

In some embodiments, the intermediate polyester can be reacted with apolyepoxy compound to form the desired polyester anticrater agent.Suitable polyepoxy compounds can have an epoxy group equivalency of, onaverage, two or more. In some embodiments, the polyepoxy compounds canbe saturated, unsaturated, cyclic, alicyclic, aliphatic, cycloaliphatic,aromatic or heterocyclic. In further embodiments, the polyepoxycompounds can also contain substituents such as, for example, halogens,hydroxyl groups, ethers, alkyl and/or aryl groups provided that thesubstituents do not adversely affect the reactivity of the epoxy groupor the properties of the resulting polyester.

Suitable polyepoxy compounds can include, for example, the glycidylethers of polyols, especially, cyclic polyols and/or aromatic polyols.In some examples, these can include, the polyglycidyl ethers of1,1-bis-(4-hydroxyphenyl) ethane, 1,1-bis-(4-hydroxyphenyl) propane,2,2-bis-(4-hydroxyphenyl) propane,2,2-bis(4-hydroxy-3-tertiarybutylphenyl)propane, bis-(4-hydroxyphenyl)methane, bis-(2-hydroxyphenyl) methane, 1,4-dihydroxy naphthalene,1,5-dihydroxy naphthalene, 1,2-bis(hydroxymethyl)cyclohexane,1,3-bis-(hydroxymethyl)cyclohexane, 1,4-bis(hydroxymethyl)cyclohexane,1,2-cyclohexane diol, 1,4-cyclohexane diol, hydrogenated bisphenol A,trimethylol propane, pentaerythritol and a combination thereof.

In some embodiments, the polyepoxy compounds can have a molecular weightin the range of from 100 to 3,000 Daltons and in further embodiments,can have a molecular weight in the range of from 340 to 2,000 Daltons.

The intermediate polyester can be contacted with polyepoxide compound ata temperature in the range of from 20° C. to 150° C., optionally in thepresence of a catalyst and/or organic solvent for 10 minutes to 24 hoursto give the desired polyester anticrater agent. In some embodiments, thecompletion of the reaction can be measured by the disappearance of theepoxide peak as measured by infrared radiation. In some embodiments, acatalyst can be used during the formation of the polyester. Suitablecatalysts can include for example, triarylphosphines,triphenylphosphine, alkyltriarylphosphonium halides,ethyltriphenylphosphonium halide, alkyltriarylphosphonium esters,ethyltriphenylphosphonium acetate, ethyltriphenylphosphonium diacetate,tetraalkylphosphonium halide or a combination thereof. The viscosity ofthe polyester can be adjusted by adding or removing organic solvent asneeded.

The anticrater additive can be used with cathodic electrocoatingcompositions that are typically used in the automotive industry. Suchelectrocoating compositions comprise an aqueous emulsion having filmforming binders dispersed therein. The film forming binders can compriseany of the known electrocoating crosslinkable components andcrosslinking agents. In some embodiments, the crosslinkable componentcomprises or consists essentially of an epoxy amine adduct and thecrosslinking agent comprises or consists essentially of blockedpolyisocyanates.

To disperse the non-water reducible anticrater agent in theelectrocoating composition, the anticrater agent can be combined withthe crosslinkable component and the crosslinking agent and mixed. Insome embodiments, the anticrater agent can be used in an amount in therange of from 0.5 to 10 percent by weight, based on the weight of thecrosslinkable component and the crosslinking agent. In otherembodiments, the anticrater agent can be used in an amount in the rangeof from 1 to 5 percent by weight, based on the weight of thecrosslinkable component and the crosslinking agent. In some embodiments,the anticrater agent can be used in an amount in the range of from 0.5to 10 percent by weight, based on the weight of the epoxy amine adductand the blocked polyisocyanate crosslinking agent. In still furtherembodiments, the anticrater agent can be used in an amount in the rangeof from 1 to 5 percent by weight, based on the weight of the epoxy amineadduct and the blocked polyisocyanate crosslinking agent.

After mixing the anticrater agent with the epoxy amine adduct and thecrosslinking agent, an aqueous acid can be added. The aqueous acid formsan ammonium salt with the epoxy amine adduct, producing a water solubleor water dispersible mixture which is known as the principal emulsion.While not wishing to be bound by theory, it is thought that the acid ofthe aqueous acid used to form the principal emulsion is a stronger acidthan any remaining acid groups of the polyester anticrater agent. If anyacid functional groups remain on the polyester anticrater agent, andthose acid groups form a salt with the epoxy amine adduct, it isbelieved that the acid groups of the aqueous acid would then displacethem regenerating the original polyester anticrater agent with free acidgroups.

The principal emulsion can then be combined with known pigment pastes,coalescing solvents and other additives that are common in the art toform the electrocoating composition. The electrocoating composition isplaced in an insulated tank containing the anode. The object to becoated is made the cathode and is passed through the tank containing theelectrocoating composition. The thickness of the coating is a functionof the bath characteristics, the electrical operating characteristics,the immersion time, and so forth. After coating, the object is removedfrom the bath and can be rinsed with deionized water. The appliedcoating can then be cured in an oven at sufficient temperature toproduce crosslinking. Usually the cured electrocoat composition isovercoated with any of a variety of different topcoat systems (e.g.basecoat/clearcoat) as is known in the art.

Another embodiment of the present disclosure is a substrate that iscoated with a dried and cured layer of the improved electrocoatingcomposition. In these embodiments, a substrate is coated with a layer ofthe electrocoating composition comprising the anticrater additive andthe applied layer is dried and cured to produce a crosslinked coating ona substrate. The step of curing can take place in a curing oven at atemperature in the range of from 150° C. to 190° C. for 10 to 60minutes. The cured coating layer can have a dry film thickness in therange of from 10 micrometers to 30 micrometers.

Suitable substrates can include any electrically conductive material,especially those for an automobile vehicle or body. Non-conductivesubstrates that have been made electrically conductive by the additionof a conductive coating can also be coated.

Examples

A highly branched non water-reducible polyester was prepared by charging266 parts dodecenylsuccinic anhydride, 130 parts 2-ethylhexanol, 244parts glycidyl ester of neodecanoic acid and 2 parts triphenylphosphineinto a suitable reaction vessel and heated to 116° C. under a nitrogenblanket. The reaction was held at 132° C. until essentially all of epoxygroup was reacted as indicated by titration method. 266 partsdodecenylsuccinic anhydride and 2 parts triphenylphosphine were addedand held at 132° C. until an acid number of 55 mg KOH per g of sample orgreater was achieved. 181 parts EPON® 828 (epoxy resin with 188 EEW) and2 parts triphenylphosphine were charged into the reaction vessel. Thereaction mixture was held at 132° C. until all of the epoxy resin wasreacted as indicated by titration method. 263 parts methyl isobutylketone was added. The resulting resin solution had a nonvolatile of 80%in methyl isobutyl ketone.

What is claimed is:
 1. An improved cathodic electrocoating composition,comprising an aqueous emulsion having dispersed therein a crosslinkablecomponent and a crosslinking agent and further comprising a non-waterreducible anticrater agent comprising a polyester which is the reactionproduct of (d) a polyepoxy compound and an intermediate polyester whichis the reaction product of a monomer mixture consisting of (a) a cyclicaliphatic carboxylic acid anhydride, (b) a monofunctional epoxycompound, and (c) a monofunctional alcohol wherein the cyclic aliphaticcarboxylic acid anhydride comprises one or more side chains selectedfrom the group consisting of an alkyl side chain having in the range offrom 6 to 20 carbon atoms, an alkenyl side chain having in the range offrom 6 to 20 carbon atoms and a combination thereof, wherein thenon-water reducible anticrater agent has a solubility in water of lessthan 0.5 grams/liter, and wherein the intermediate polyester has amolecular weight per epoxy group of greater than 15,000 Daltons.
 2. Thecomposition of claim 1, wherein the aliphatic carboxylic acid anhydridehas a structure according to formula (I);

wherein each R is independently selected from the group consisting of alinear alkyl or alkenyl group having in the range of from 6 to 20 carbonatoms or a branched alkyl or alkenyl group having in the range of from 6to 20 carbon atoms; each R¹ is independently selected from the groupconsisting of hydrogen, a linear alkyl or alkenyl group having in therange of from 6 to 20 carbon atoms, or a branched alkyl or alkenyl grouphaving in the range of from 6 to 20 carbon atoms; or wherein R and R¹may be taken together to form a ring having in the range of from 5 to 6carbon atoms wherein the ring may optionally be substituted with alinear or branched alkyl group having in the range of from 1 to 18carbon atoms or a linear or branched alkenyl group having in the rangeof from 2 to 18 carbon atoms; n is in the range of from 1 to 2; and q isin the range of from 1 to
 2. 3. The composition of claim 1 wherein themonofunctional alcohol contains in the range of from 4 to 12 carbonatoms and is a linear, branched or cycloaliphatic alcohol.
 4. Thecomposition of claim 3 wherein the monofunctional alcohol is chosen fromthe group consisting of hexanol, 2-methyl butanol, 2-ethylhexanol,cyclohexyl methanol, methyl cyclohexanol, cyclohexanol, octanol and acombination thereof.
 5. The composition of claim 1 wherein themonofunctional epoxy is an epoxy ester or an epoxy ether.
 6. Thecomposition of claim 5 wherein the monofunctional epoxy is the glycidylester of a carboxylic acid wherein the carboxylic acid has a structureaccording to formula (II);

wherein each R³, R⁴ and R⁵ is independently selected from the groupconsisting of a linear alkyl group having in the range of from 1 to 12carbon atoms, a branched alkyl group having in the range of from 3 to 12carbon atoms, a cycloaliphatic alkyl group having in the range of from 5to 8 carbon atoms or a combination thereof.
 7. The composition of claim1 wherein the polyepoxy compound is chosen from the group consisting ofpolyglycidyl ethers of 1,1-bis-(4-hydroxyphenyl)ethane,1,1-bis-(4-hydroxyphenyl)propane, 2,2-bis-(4-hydroxyphenyl)propane,2,2-bis(4-hydroxy-3-tertiarybutylphenyl)propane,bis-(4-hydroxyphenyl)methane, bis-(2-hydroxyphenyl)methane,1,4-dihydroxy naphthalene, 1,5-dihydroxy naphthalene,1,2-bis(hydroxymethyl)cyclohexane, 1,3-bis-(hydroxymethyl)cyclohexane,1,4-bis(hydroxymethyl)cyclohexane, 1,2-cyclohexane diol, 1,4-cyclohexanediol, hydrogenated bisphenol A, trimethylol propane, pentaerythritol ora combination thereof.
 8. The composition of claim 1 wherein thecathodic electrocoat composition contains in the range of from 0.5 to 10percent by weight of the anticrater agent, wherein the weight percentageis based on the amount of the crosslinkable component and thecrosslinking agent.
 9. The composition of claim 8 wherein thecrosslinkable component is an epoxy amine adduct and the crosslinkingagent is a blocked polyisocyanate.
 10. The composition of claim 1,wherein the non-water reducible anticrater agent has a solubility inwater of less than 0.1 grams/liter.
 11. The composition of claim 1,wherein the molecular weight per epoxy group is greater than 17,000Daltons.
 12. The composition of claim 1, wherein the molecular weightper epoxy group is greater than 18,000 Daltons.
 13. A coated substrate,the coated substrate being coated with layer of an improved cathodicelectrocoating composition comprising an aqueous emulsion havingdispersed therein a crosslinkable component and a crosslinking agent,and further comprising a non-water reducible anticrater agent comprisinga polyester which is the reaction product of (d) a polyepoxy compoundand an intermediate polyester which is the reaction product of a monomermixture consisting of (a) a cyclic aliphatic carboxylic acid anhydride,(b) a monofunctional epoxy compound, and (c) a monofunctional alcoholwherein the cyclic aliphatic carboxylic acid anhydride comprises one ormore side chains selected from the group consisting of an alkyl sidechain having in the range of from 6 to 20 carbon atoms, an alkenyl sidechain having in the range of from 6 to 20 carbon atoms and a combinationthereof, wherein the non-water reducible anticrater agent has asolubility in water of less than 0.5 grams/liter, and wherein theintermediate polyester has a molecular weight per epoxy group of greaterthan 15,000 Daltons.
 14. An improved cathodic electrocoatingcomposition, comprising an aqueous emulsion having dispersed therein acrosslinkable component and a crosslinking agent, and further comprisinga non-water reducible anticrater agent comprising a polyester which isthe reaction product of (d) a polyepoxy compound and an intermediatepolyester which is the reaction product of a monomer mixture consistingof (a) a cyclic aliphatic carboxylic acid anhydride, (b) amonofunctional epoxy compound, and (c) a monofunctional alcohol whereinthe cyclic aliphatic carboxylic acid anhydride comprises one or moreside chains selected from the group consisting of an alkyl side chainhaving in the range of from 6 to 20 carbon atoms, an alkenyl side chainhaving in the range of from 6 to 20 carbon atoms and a combinationthereof, and wherein the intermediate polyester comprises epoxy groups.15. The composition of claim 12, wherein the non-water reducibleanticrater agent has a solubility in water of less than 0.5 grams/liter.